Production of ZA-27 Alloy by New Rheocasting Process


  • Adnan Naama Abood Technical College, Baghdad, Iraq. Author
  • Tahar Salah Habeb Technical College, Baghdad, Iraq. Author



New Rheocasting, Zn-Al alloy, Pouring Temperature, Quenching Temperature, Equaxial Grain, Mechanical Properties


The present work encompasses the grains refining of microstructure of Zn-Al alloy (ASTM B669 ZA-27) ingots without addition of refining agents or using stirring, that is, by using the New Rheocasting (NRC). AISI 316 stainless steel mould is employed with inclination angle of 75o and 1.2 V/A ratio. The pouring temperatures are 532 oC, 522 oC, and 502 oC, while the quenching occurs at different temperatures. The examination shows that all NRC ingots have microstructure of refined equaxial grains in the range of 27- 36 μm, while the percentage of volume fraction of α-Al phase was varied from 0.56 to 0.76. The value of circularity was in the range of 1.33-1.65. The NRC ingots achieved less coarsening kinetic than critical value which shows that there is a limited increase in the grain size and coalescence of reheating. Tensile strength, Yield strength, and Elongation of ZA-27 alloy which was made by NRC process, increased to 18%, 11%, and 32% respectively compare to Gravity Die Casting (GDC) ingots due to formation of equaxil grains along all the cross section in addition to smaller grains size.


Kaufmann, H. & Wabusseg, H., "Metallurgical and processing aspect of NRC semi– solid casting technology", Aluminum, 2000, 76,. 69-75.

Young, K. & Eisen, P.,"SSM technological alternatives for different application ", Metallurgical Science and Technology, 2000, 18, 11-15.

Winterbottom, W. L., "Semi–solid forming application high volume automotive products", Metallurgical Science and Technology , 2000, 18,. 5-10.

Kleiner, S. & Beffort, O. , "Microstructure and mechanical properties of squeeze cast and semi–solid cast Mg–Al alloys" , Journal of Light Metals, 2002, 277-280 DOI:

Flemings, M. C., "Behavior of metal alloys in the semisolid state" Metallurgical transactions B, Vol .22B, 1991, 269-292. DOI:

Kirkwood, D. H. , "Semi-solid processing of high melting point alloy" , proceedings of the 4th International Conference on Semi-solid Processing of Alloys and Composites ,Sheffield , 1996, 320-325.

Tzimas, E., "Evaluation of Volume Fraction of Solid in alloys Formed by semisolid processing" Journal of Materials Science 2000, 5319-5329. DOI:

Yurko, James A. & Raul, A., "Commercial development of the Semi-Solid Rheocasting process "Metallurgical Science and Technology". 2003, 21 (1), 10-15.

Abood, Adnan .N., "Design and Characterization of Advanced semi – solid casting processes" a thesis of PhD submitted to the Department of Production Engineering and Metallurgy University of Technology, IRAQ , 2003.

Zhang, B.& Garro, M., " Dendrite Arm Spacing in Aluminum alloy cylinder heads produced by gravity Semi-Permanent mold, Metallurgical Science and Technology 2003, 21, ( 1), 3-9.

Rice, Chris S. & Mendez, Patricio F., “Slurry-Based Semi- Solid Casting”, Advanced Materials and Processes, 2001, 159, (10).Flemings, M. C.," Solidification processing", McGraw–Hill, New York, 1974.



How to Cite

Production of ZA-27 Alloy by New Rheocasting Process. (2008). Journal of Zankoy Sulaimani - Part A, 11(1), 89-99.

Most read articles by the same author(s)

1 2 3 4 5 6 7 8 9 10 > >>